UNS S31000 AISI 310 Stainless steel

This data sheet applies to stainless steel 310 / 1.4845 hot and cold rolled sheet, strip and bars, semi-finished products, rods and sections as well as for seamless and welded steel tubes for mechanical and general engineering purposes.

Application

For construction parts which should be resistant to scaling up to about 1050°C and extensively inured to the effect of sulfurous gases, especially above 900°C, is very low.

Chemical Compositions

Element	% Present (in product form)
	C, H, P, L	TW* / TS*
Carbon (C)	≤0.10	≤0.15
Silicon (Si)	≤1.50	≤0.75
Manganese (Mn)	≤2.00	≤2.00
Phosphorous (P)	≤0.045	≤0.045
Sulfur (S)	≤0.015	≤0.030
Chromium (Cr)	24.00 - 26.00	24.00 - 26.00
Nickel (Ni)	19.00 - 22.00	19.00 - 22.00
Nitrogen (N)	≤0.11	-
Iron (Fe)	Balance	Balance

Mechanical properties _{(at room temperature in annealed condition)}

			Product Form
			C, H, P	L	TW* / TS*
Thickness a or diamter d (mm)			a ≤ 12	d ≤ 25	-
Hardness HB max. ^{1) 2) 3)}			192	192	-
Proof Strength³⁾		R_p0.2 N/mm²	210	210	230
Proof Strength³⁾		R_p1.0 N/mm²	230	230	270
Tensile Strength		R^m N/mm²	500 - 700	500 - 700	min. 500
Elongation min. in %	Long Products		35¹⁾	35¹⁾	33⁴⁾ / 35^₅₎
	Flat Products	0.5 ≤ a/d < 3	33⁴⁾⁵⁾	33⁴⁾⁵⁾	35⁴⁾⁵⁾⁶⁾
	Flat Products	3 ≤ a/d	35⁴⁾⁵⁾	35⁴⁾⁵⁾	35⁴⁾⁵⁾⁶⁾

Creep Properties _{(estimated average values about the long-term behaviour at elevated temperature^*)}

	1% Elongation¹⁾ for		Rupture²⁾ for
Temperature °C	1,000 h N/mm²	10,000 h N/mm²	1,000 h N/mm²	10,000 h N/mm²	100,000 h N/mm²
600	100	90	170	130	80
700	45	30	80	40	18
800	18	10	35	18	7
900	10	4	15	8.5	3

Reference data on some physical properties

Density at 20°C kg/m³		7.9
Thermal Conductivity W/m K at	20°C	15
Thermal Conductivity W/m K at	500°C	19
Specific Thermal Capacity at 20°C J/kg K		500
Electrical Resistivity at 20°C Ω mm² /m		0.85

Coefficient of linear thermal expansion 10^-6 K^-1 between 20°C and

200°C	15.5
400°C	17.0
600°C	17.5
800°C	18.5
1000°C	19.0