S31668 0Cr17Ni12Mo2Ti Stainless steel
This data sheet applies to stainless steel 316Ti / 1.4571 hot and cold rolled sheet and strip, semi-finished products, bars and rods, wire and sections as well as for seamless and welded tubes for pressure purposes.
Construction encasement, doors, windows and armatures, off-shore modules, container and tubes for chemical tankers, warehouse and land transportation of chemicals, food and beverages, pharmacy, synthetic fibre, paper and textile plants and pressure vessels. Due to the Ti-alloy, resistance to intergranular corrosion is guaranteed after welding.
| Element | % Present (in product form) | |||
|---|---|---|---|---|
| C, H, P | L | TW | TS | |
| Carbon (C) | 0.08 | 0.08 | 0.08 | 0.08 |
| Silicon (Si) | 1.00 | 1.00 | 1.00 | 1.00 |
| Manganese (Mn) | 2.00 | 2.00 | 2.00 | 2.00 |
| Phosphorous (P) | 0.045 | 0.045 | 0.0453) | 0.040 |
| Sulfur (S) | 0.0151) | 0.0301) | 0.0153) | 0.0151) |
| Chromium (Cr) | 16.50 - 18.50 | 16.50 - 18.50 | 16.50 - 18.50 | 16.50 - 18.50 |
| Nickel (Ni) | 10.50 - 13.50 | 10.50 - 13.502) | 10.50 - 13.50 | 10.50 - 13.502) |
| Molybdenum (Mo) | 2.00 - 2.50 | 2.00 - 2.50 | 2.00 - 2.50 | 2.00 - 2.50 |
| Titanium (Ti) | 5xC to 070 | 5xC to 070 | 5xC to 070 | 5xC to 070 |
| Iron (Fe) | Balance | Balance | Balance | Balance |
| Product Form | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| C | H | P | L | L | TW | TS | |||
| Thickness (mm) Max | 8 | 12 | 75 | 160 | 2502) | 60 | 60 | ||
| Yield Strength | Rp0.2 N/mm2 | 2403) | 2203) | 2203) | 2004) | 2005) | 1906) | 1906) | |
| Rp1.0 N/mm2 | 2703) | 2603) | 2603) | 2354) | 2355) | 2256) | 2256) | ||
| Tensile Strength | Rm N/mm2 | 540 - 6903) | 540 - 6903) | 520 - 6703) | 500 - 7004) | 500 - 7005) | 490 - 6906) | 490 - 6906) | |
| Elongation min. in % | A1) %min (longitudinal) | - | - | - | 40 | - | 35 | 35 | |
| A1) %min (transverse) | 40 | 40 | 40 | - | 30 | 30 | 30 | ||
| Impact Energy (ISO-V) ≥ 10mm thick | Jmin (longitudinal) | - | 90 | 90 | 100 | - | 100 | 100 | |
| Jmin (transverse) | - | 60 | 60 | 0 | 60 | 60 | 60 | ||
| Density at 20°C kg/m3 | 8.0 | |
|---|---|---|
| Modulus of Elasticity kN/mm2 at | 20°C | 200 |
| 200°C | 186 | |
| 400°C | 172 | |
| 500°C | 165 | |
| Thermal Conductivity W/m K at 20°C | 15 | |
| Specific Thermal Capacity at 20°C J/kg K | 500 | |
| Electrical Resistivity at 20°C Ω mm2 /m | 0.75 | |
| 100°C | 16.5 |
|---|---|
| 200°C | 17.5 |
| 300°C | 18.0 |
| 400°C | 18.5 |
| 500°C | 19.0 |