Mechanical Properties
| Temper | Annealed | Cold worked | ||
|---|---|---|---|---|
| Tensile Rm | 75 | ksi (min) | 125 | ksi (min) |
| Tensile Rm | 515 | MPa (min) | 860 | MPa (min) |
| R.p. 0.2% Yield | 30 | ksi (min) | 100 | ksi (min) |
| R.p. 0.2% Yield | 205 | MPa (min) | 690 | MPa (min) |
| Elongation (2" or 4D gl) | 35 | % (min) | 15 | % (min) |
Physical Properties (Room Temperature)
| Specific Heat (0-100°C) | 485 | J.kg-1.°K-1 |
| Thermal Conductivity | 16.3 | W.m -1.°K-1 |
| Thermal Expansion | 16.5 | μm/μm/°C |
| Modulus Elasticity | 200 | GPa |
| Electrical Resistivity | 7.4 | μohm/cm |
| Density | 7.99 | g/cm3 |
Chemical Composition (% by weight)
| Element | Min | Max |
|---|---|---|
| C | - | 0.03 |
| Mn | - | 2 |
| Ni | 13 | 15 |
| Cr | 17 | 19 |
| Mo | 2 | 3 |
| S | - | 0.1 |
| Si | - | 0.75 |
| P | - | 0.25 |