0Cr18Ni10Ti SUS321 Stainless steel
This data sheet applies to stainless steel 321 / 1.4541 hot and cold rolled sheet and strip, semi-finished products, bars, rolled wire and profiles as well as seamless and welded tubes for pressure purposes.
Instruments and construction parts in the food industry, luxury food, film and photo industry as well as for articles of daily use in the household, power station construction. Due to the Ti-alloy, the resistance to intergranular corrosion is also guaranteed in the welded condition.
| Element | % Present (in product form) | |||
|---|---|---|---|---|
| C, H, P | L | TW | TS | |
| Carbon (C) | ≤0.08 | ≤0.08 | ≤0.08 | ≤0.08 |
| Silicon (Si) | ≤1.00 | ≤1.00 | ≤1.00 | ≤1.00 |
| Manganese (Mn) | ≤2.00 | ≤2.00 | ≤2.00 | ≤2.00 |
| Phosphorous (P) | ≤0.045 | ≤0.045 | ≤0.0453) | ≤0.040 |
| Sulfur (S) | ≤0.0151) | ≤0.0301) | ≤0.0153) | ≤0.0151) |
| Chromium (Cr) | 17.00 - 19.00 | 17.00 - 19.00 | 17.00 - 19.00 | 17.00 - 19.00 |
| Nickel (Ni) | 9.00 - 12.00 | 9.00 - 12.002) | 9.00 - 12.00 | 9.00 - 12.002) |
| Titanium (Ti) | 5xC to 0.70 | 5xC to 0.70 | 5xC to 0.70 | 5xC to 0.70 |
| Iron (Fe) | Balance | Balance | Balance | Balance |
| Product Form | Max Thickness (mm) | Yield Strength | Tensile Strength | Elongation min. in % | Impact Energy (ISO-V) ≥ 10mm thick | |||
|---|---|---|---|---|---|---|---|---|
| 0.2% Rp0.2 N/mm2 | 1% Rp1.0 N/mm2 | Rm N/mm2 | A1) %min (longitudinal) | A1) %min (transverse) | Jmin (longitudinal) | Jmin (transverse) | ||
| C | 8 | 2203) | 2203) | 520-7203) | - | 40 | - | - |
| H | 13.5 | 2003) | 2403) | 520-7203) | - | 40 | 100 | 60 |
| P | 75 | 2003) | 2403) | 500-7003) | - | 40 | 100 | 60 |
| L | 160 | 1904) | 2254) | 500-7004) | 40 | - | 100 | - |
| L | 2502) | 1907) | 2257) | 500-7007) | - | 30 | - | 60 |
| TW | 60 | 1805) | 2155) | 460-6805) | 35 | 30 | 100 | 60 |
| TS | 60 | 1805) | 2155) | 460-6805) | 35 | 30 | 100 | 60 |
| Density at 20°C kg/m3 | 7.9 | |
|---|---|---|
| Modulus of Elasticity kN/mm2 at | 20°C | 200 |
| 200°C | 186 | |
| 400°C | 172 | |
| 500°C | 165 | |
| Thermal Conductivity W/m K at 20°C | 15 | |
| Specific Thermal Capacity at 20°C J/kg K | 500 | |
| Electrical Resistivity at 20°C Ω mm2 /m | 0.73 | |
| 100°C | 16.0 |
|---|---|
| 200°C | 16.5 |
| 300°C | 17.0 |
| 400°C | 17.5 |
| 500°C | 18.0 |