Subcategories: Carbon Steel; AISI 1000 Series Steel; Low Carbon Steel
Close Analogs:
Key Words: UNS G10260, ASTM A29, ASTM A273, ASTM A510, ASTM A519, ASTM A545, ASTM A576, carbon steels
| Component | Weight % | |||||
| C | Max 0.28 | |||||
| Fe | 98.73-99.18 | |||||
| Mn | 0.60-0.90 | |||||
| P | Max 0.040 | |||||
| S | Max 0.050 | |||||
| Physical Properties | Metric | English | Comments | Cold Head | Hot Forge | Wire Form |
| Density | 7.858 g/cc | 0.2839 lb/in³ | ||||
| Mechanical Properties | Metric | English | Comments | Cold Head | Hot Forge | Wire Form |
| Hardness, Brinell | 143 | 143 | ||||
| Hardness, Knoop | 163 | 163 | Converted from Brinell hardness. | |||
| Hardness, Rockwell B | 78 | 78 | Converted from Brinell hardness. | |||
| Hardness, Vickers | 149 | 149 | Converted from Brinell hardness. | |||
| Tensile Strength, Ultimate | 490 MPa | 71100 psi | ||||
| Tensile Strength, Yield | 415 MPa | 60200 psi | ||||
| Elongation at Break | 15% | 15% | In 50 mm | |||
| Reduction of Area | 40% | 40% | ||||
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical for steel | |||
| Bulk Modulus | 160 GPa | 23200 ksi | Typical for steel | |||
| Poissons Ratio | 0.29 | 0.29 | Typical For Steel | |||
| Machinability | 75.00% | 75.00% | Based on AISI 1212 steel. as 100% machinability | |||
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel | |||
| Electrical Properties | Metric | English | Comments | Cold Head | Hot Forge | Wire Form |
| Electrical Resistivity | 0.0000169 ohm-cm | 0.0000169 ohm-cm | ||||
| Thermal Properties | Metric | English | Comments | Cold Head | Hot Forge | Wire Form |
| CTE, linear | 12.1 µm/m-°C | 6.72 µin/in-°F | ||||
| @Temperature 0.000 – 100 °C | @Temperature 32.0 – 212 °F | |||||
| 13.3 µm/m-°C | 7.39 µin/in-°F | |||||
| @Temperature 0.000 – 300 °C | @Temperature 32.0 – 572 °F | |||||
| 14.4 µm/m-°C | 8.00 µin/in-°F | |||||
| @Temperature 0.000 – 500 °C | @Temperature 32.0 – 932 °F | |||||
| Specific Heat Capacity | 0.486 J/g-°C | 0.116 BTU/lb-°F | ||||
| @Temperature >=100 °C | @Temperature >=212 °F | |||||
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F |