Stainless martensitic steel with a high hardenability, good polishing properties, excellent resistance to corrosion and hot oxidation.

Application:

Used for plastic moulds, particularly for acid aggressive plastics (e.g. acetate and PVC), or plastics containing abrasive fillers. Suited for the manufacture of glass, such as moulds of optical products.

Comparable Standards:                                                                                                                                    

 Chemical Analysis (%):                                                                                                                                    

Heat treatment                                                                                                                                                   

Annealing:

-Heat to 750~800°C, with hold at minimum rate for 3 hours.

-Furnace cooling.

Stress relieving:

To be carried out after machining and before the final heat treatment.

Heating to 600~650°C for 2 hours.

Hardening:

Preheating to 600~700°C;

- Austenitizing at 990~1040°C

- Oil or thermal bath cooling at 500~550°C, then oil cooling according to the steel shape and size.

Quenched hardness: HRC 52~56