| Chemical Element | % Present |
|---|---|
| Manganese (Mn) | 0.0 - 0.50 |
| Iron (Fe) | 0.0 - 0.35 |
| Magnesium (Mg) | 0.40 - 0.70 |
| Silicon (Si) | 0.50 - 0.90 |
| Zinc (Zn) | 0.0 - 0.20 |
| Titanium (Ti) | 0.0 - 0.10 |
| Chromium (Cr) | 0.0 - 0.30 |
| Copper (Cu) | 0.0 - 0.30 |
| Manganese + Chromium (Mn+Cr) | 0.12 - 0.50 |
| Other (Each) | 0.0 - 0.05 |
| Others (Total) | 0.0 - 0.15 |
| Aluminium (Al) | Balance |
| Physical Property | Value |
|---|---|
| Density | 2.70 g/cm³ |
| Melting Point | 605 °C |
| Thermal Expansion | 24 x10^-6 /K |
| Modulus of Elasticity | 70 GPa |
| Thermal Conductivity | 188 W/m.K |
| Electrical Resistivity | 0.034 x10^-6 Ω .m |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 225 Min MPa |
| Tensile Strength | 270 Min MPa |
| Elongation A50 mm | 8 % |
| Shear Strength | 205 MPa |
| Hardness Brinell | 90 HB |
| Elongation A | 10 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 225 Min MPa |
| Tensile Strength | 270 Min MPa |
| Hardness Brinell | 90 HB |
| Elongation A | 8 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 215 Min MPa |
| Tensile Strength | 260 Min MPa |
| Hardness Brinell | 85 HB |
| Elongation A | 8 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 225 Min MPa |
| Tensile Strength | 270 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 90 HB |
| Elongation A | 8 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 215 Min MPa |
| Tensile Strength | 260 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 85 HB |
| Elongation A | 8 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 225 Min MPa |
| Tensile Strength | 270 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 90 HB |
| Elongation A | 8 Min % |
| Mechanical Property | Value |
|---|---|
| Proof Stress | 215 Min MPa |
| Tensile Strength | 260 Min MPa |
| Elongation A50 mm | 6 Min % |
| Hardness Brinell | 85 HB |
| Elongation A | 8 Min % |